Compound semiconductor device and doherty amplifier using compound semiconductor device

ABSTRACT

A lower electron supply layer is disposed over a lower electron transport layer made of compound semiconductor. The lower electron supply layer is made of n-type compound semiconductor having an electron affinity smaller than that of the lower electron transport layer. An upper electron transport layer is disposed over the lower electron supply layer. The upper electron transport layer is made of compound semiconductor having a doping concentration lower than that of the lower electron supply layer or non-doped compound semiconductor. An upper electron supply layer is disposed over the upper electron transport layer. The upper electron supply layer is made of n-type compound semiconductor having an electron affinity smaller than that of the upper electron transport layer. A source and drain electrodes are disposed over the upper electron supply layer. A gate electrode is disposed over the upper electron supply layer between the source and drain electrodes.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is based on and claims priority of Japanese PatentApplication No. 2007-048053 filed on Feb. 27, 2007; and is a Divisionalof prior application Ser. No. 12/071,219 filed on Feb. 19, 2008, theentire contents of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

A) Field of the Invention

The present invention relates to a compound semiconductor device and aDoherty amplifier using the compound semiconductor device, and moreparticularly to a Doherty amplifier using field effect transistors, anda compound semiconductor device applicable to a peak amplifier of theDoherty amplifier.

B) Description of the Related Art

Developments are made vigorously in an electronic device which hascrystalline AlGaN/GaN grown on a substrate made of sapphire, siliconcarbide (SiC), gallium nitride (GaN) or silicon (Si), and uses a GaNlayer as an electron transport layer (e.g., JP-A-2006-165207). GaN has aband gap of 3.4 eV and is expected to operate at higher breakdownvoltage than GaAs having a band gap of 1.4 eV. If a high electronmobility transistor (HEMT) made of GaN and having a high breakdownvoltage is used as an amplifier, this amplifier can operate along a loadline corresponding to large load impedance on a graph showingcurrent-voltage characteristic. A high efficiency operation is thereforepossible.

A base station amplifier for world interoperability for microwave access(WiMAX) requires a nonconventional high efficiency. In order to realizea high efficiency, use of Doherty amplifiers has been studied (Forexample, JP-A-2006-166141).

FIG. 1 is a fundamental equivalent circuit diagram of a Dohertyamplifier. A high frequency signal input from an input terminal Ti isdivided into two parts. One part is input to a carrier (main) amplifier100 and the other part is input to a peak (auxiliary) amplifier 101 viaa quarter-wave line 103. Another quarter-wave line 102 is connected toan output terminal of the carrier amplifier 100. An output signal of thecarrier amplifier 100 passes through the quarter-wave line 102 andthereafter is combined with an output signal of the peak amplifier 101.A load impedance R_(L) is connected to an output terminal To. Thecarrier amplifier 100 is biased to operate as class A or class AB, andthe peak amplifier 101 is biased so that an idle current is smaller thanthat of the carrier amplifier 100.

FIG. 9 shows an example of input/output characteristics of a Dohertyamplifier. In FIG. 9, a solid line ac and a broken line ap0 indicate theinput/output characteristics of the carrier amplifier 100 and peakamplifier 101, respectively. A solid line at indicates the input-outputcharacteristics of the Doherty amplifier including the carrier amplifier100 and peak amplifier 101.

When an input power is small and the Doherty amplifier operates in theback-off region, mainly the carrier amplifier 100 operates and outputsan output signal. When the input power is sufficiently large and anoutput power of the carrier amplifier 100 saturates, the peak amplifier101 operates and outputs an output signal. During the operation in theback-off region, a d.c. consumption power of the peak amplifier 101 issufficiently small. An efficiency of the Doherty amplifier itself istherefore high. Since output signals of the carrier amplifier 100 andpeak amplifier 101 are combined, a large output power can be obtained.

It has been found that if a HEMT using GaN are applied to the carrieramplifier 100 and peak amplifier 101 of the Doherty amplifier, anefficiency of the Doherty amplifier is not improved so much as expected.This is because even if an idle current of the peak amplifier 101 ismade small, a gain profile of the peak amplifier 101 is similar to thatof the carrier amplifier 100. With similar gain profiles of both of theamplifiers, even if the Doherty amplifier operates in the back-offregion, a gain of the peak amplifier 101 is large and a d.c. componentof an output signal of the peak amplifier 101 is large. The efficiencyis therefore not improved so much as expected.

While the carrier amplifier 100 operates in a saturated state, aSchottky barrier between a gate electrode and a substrate lowers, and aforward gate leak current increases. If the Doherty amplifier hasdistortion compensation, this distortion compensation is disabled by thegate leak current.

SUMMARY OF THE INVENTION

According to one aspect of the an embodiment, there is provided acompound semiconductor device including:

a lower electron transport layer made of compound semiconductormaterial;

a lower electron supply layer disposed over the lower electron transportlayer and made of compound semiconductor material doped to n-type andhaving an electron affinity smaller than an electron affinity of thelower electron transport layer;

an upper electron transport layer disposed over the lower electronsupply layer and made of compound semiconductor material having a dopingconcentration lower than a doping concentration of the lower electronsupply layer or non-doped compound semiconductor material;

an upper electron supply layer disposed over the upper electrontransport layer and made of n-type compound semiconductor materialhaving an electron affinity smaller than an electron affinity of theupper electron transport layer;

a source electrode and a drain electrode disposed over the upperelectron supply layer at a distance from each other and being in ohmiccontact with the lower electron transport layer and the upper electrontransport layer; and

a gate electrode disposed over the upper electron supply layer betweenthe source electrode and the drain electrode.

According to another aspect of an embodiment, there is provided aDoherty amplifier using the above-described compound semiconductordevice as the peak amplifier.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an equivalent circuit diagram of a Doherty amplifier accordingto a first embodiment.

FIG. 2 is a cross sectional view of a HEMT of the first embodiment.

FIGS. 3A to 3D are cross sectional views of the HEMT during manufactureof the first embodiment.

FIG. 4 is an energy band diagram of the HEMT of the first embodiment.

FIG. 5 is a graph showing the gate voltage-drain current characteristicsof the HEMT of the first embodiment and a conventional HEMT.

FIGS. 6A and 6B are graphs showing dependency of a gain upon an inputvoltage at various idle currents, of the HEMT of the first embodimentand a conventional HEMT, respectively.

FIG. 7 is a cross sectional view of a HEMT according to a secondembodiment.

FIG. 8 is a graph showing a relation between leakage power to adjacentchannels and an output power of the HEMT of the second embodiment and aHEMT having a Schottky gate structure.

FIG. 9 is a graph showing the input/output characteristics of thecarrier amplifier and peak amplifier of a Doherty amplifier and theinput/output characteristics of the Doherty amplifier including thecarrier amplifier and peak amplifier.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

FIG. 1 is an equivalent circuit diagram of a Doherty amplifier accordingto the first embodiment. Since the fundamental structure has alreadybeen described, redundant duplicates are avoided here. Each of thecarrier amplifier 100 and peak amplifier 101 includes a HEMT using GaNas the material of an electron transport layer. Bias circuits 104 and105 apply a d.c. gate bias voltage to respective gates of HEMT'sconstituting the carrier amplifier 100 and peak amplifier 101.

FIG. 2 is a cross sectional view of the HEMT to be applied to the peakamplifier 101. An underlie layer 2 made of AlN and having a thickness of0.3 μm is formed on a substrate 1 made of single crystal SiC. On theunderlie layer 2, a lower electron transport layer 3, a lower electronsupply layer 4, an upper electron transport layer 5, a non-doped layer 6and an upper electron supply layer 7 are stacked in this order.

The lower electron transport layer 3 is made of non-doped GaN and has athickness of 3 μm. The lower electron supply layer 4 is made of compoundsemiconductor material having smaller electron affinity than that of thelower electron transport layer 3, for example, n-type AlGaN doped withSi only at 2×10¹⁸ cm⁻³. The lower electron supply layer 3 has athickness of 20 nm. An atomic ratio Al/(group III element) in a regionthat is in contact with the lower electron transport layer 3 is 0.05.The atomic ratio Al/(group III element) lowers toward a shallow region,and a region that is in contact with the upper electron transport layer5 has an atomic ratio Al/(group III element) of 0.02.

The upper electron transport layer 5 is made of non-doped GaN and has athickness of 50 nm. The non-doped layer 6 is made of non-dopedAl_(0.25)Ga_(0.75)N and has a thickness of 5 nm. The upper electronsupply layer 7 is made of compound semiconductor material having asmaller electron affinity than that of the upper electron transportlayer 5, for example, n-type Al_(0.25)Ga_(0.75)N doped with Si at 4×10¹⁸cm⁻³. The upper electron supply layer has a thickness of 20 nm.

A source electrode 10 and a drain electrode 11 are disposed at adistance from each other on partial surfaces of the upper electronsupply layer 7. Each of the source electrode 10 and the drain electrode11 has a lamination structure having a Ta layer being in contact withthe upper electron supply layer 7 and an Al layer formed on the Talayer, and are in ohmic contact with the lower and upper electrontransport layers 3 and 5. A TaAl₃ layer is formed between the Ta layerand Al layer by mutual diffusion.

The surface of the upper electron supply layer 7 between the sourceelectrode 10 and drain electrode 11 is covered with a protective layer8. The protective layer 8 is made of n-type GaN doped with Si at 5×10¹⁸cm³, and has a thickness of 7 nm.

A gate electrode 12 is formed on a partial surface of the protectinglayer 8 at a distance from both the source electrode 10 and drainelectrode 11. The gate electrode 12 has a two-layer structure of a Nilayer being in contact with the protective layer 8 and an Au layerformed on the Ni layer. A gate length (a lateral size of the gateelectrode 12 in FIG. 2) is set to 0.5 μm, and a unit gate width is setto 300 μm. The “unit gate width” means a width of a region in which thegate electrode can control a density of two-dimensional electron gas. Aninsulating layer 9 covers the surfaces of the protective layer 8 betweenthe gate electrode 12 and source electrode 10 and between the gateelectrode 12 and drain electrode 11. The insulating layer 9 is made ofSiN.

Next, with reference to FIGS. 3A to 3D, description will be made on amanufacture method for the HEMT of the first embodiment.

As shown in FIG. 3A, each layer between the underlie layer 2 and theprotective layer 8 is grown on the substrate 1 made of single crystalSiC, by metal organic vapor phase epitaxy (MOVPE). For example,trimethylaluminum is used as Al source material, trimethylgallium isused as Ga source material, ammonia is used as N source material, andsilane is used as Si dopant source material.

Description will be made hereunder on processes up to the structureshown in FIG. 3B. A resist film is formed on the protective layer 8. Theresist film is exposed and developed to form openings corresponding tothe source electrode 10 and drain electrode 11. A Ta film having athickness of 10 nm and an Al film having a thickness of 280 nm aredeposited on the whole surface of the substrate by vapor deposition. Theresist film is removed together with the Ta film and Al film in theregion other than the region of the source electrode 10 and drainelectrode 11.

Next, heat treatment is performed for one minute at 550° C. in anitrogen atmosphere, using a rapid thermal anneal (RTA) apparatus. Withthis heat treatment, the TaAl₃ film is formed between the Ta film and Alfilm.

As shown in FIG. 3C, the insulating film 9 of SiN is formed on the wholesubstrate surface by plasma enhanced chemical vapor deposition (PE-CVD).

Description will be made hereunder on processes up to the structureshown in FIG. 3D. A resist film is formed on the insulating film 9. Theresist film is exposed and deposited to form an opening corresponding tothe gate electrode 12. A Ni film having a thickness of 10 nm and an Aufilm having a thickness of 200 nm are sequentially deposited on thewhole substrate surface. Next, the resist film together with the Ni filmand Au film deposited thereon is removed. In this manner, the gateelectrode 12 is formed having a two-layer structure of the Ni film andAu film.

Thereafter, as shown in FIG. 2, upper surfaces of the source electrode10 and drain electrode 11 are exposed by forming openings through theinsulating film 9. Lastly, device isolation is performed through recessetching.

FIG. 4 shows an energy band diagram of the HEMT shown in FIG. 2. Theabscissa represents a depth direction of each layer of the HEMT, and theordinate represents a potential for electrons. A curve in FIG. 4 shows apotential at the lower end of a conduction band. A one-dot chain line Efindicates a Fermi level. Piezo charges due to lattice mismatch areaccumulated at an interface between the upper electron supply layer 7and protective layer 8, at an interface between the upper electrontransport layer 5 and non-doped layer 6 and at an interface between thelower electron transport layer 3 and lower electron supply layer 4.Therefore, slopes at the conduction band lower end are not the same onboth sides of each of these interfaces.

Since electrons are accumulated at the interface between the upperelectron transport layer 5 and non-doped layer 6, an upper channel CH0consisting of two-dimensional electron gas is generated. In addition,since electrons are accumulated at the interface between the lowerelectron transport layer 3 and lower electron supply layer 4, a lowerchannel CH1 consisting of two-dimensional electron gas is generated.

In the HEMT of the first embodiment, in a state that the gate voltage is0, a two-dimensional electron gas density of the lower channel CH1 is atmost 5% of that of the upper channel CH0. A two-dimensional electron gasmobility of the lower channel CH1 is larger than 1000 cm/Vs.

FIG. 5 shows an example of gate voltage (Vg)-drain current (Id)characteristics of the HEMT of the first embodiment shown in FIG. 2. Theabscissa represents a gate voltage Vg in the unit of “V”, and theordinate represents a drain current Id in an arbitrary unit. A bold linecp in FIG. 5 shows the characteristics of the HEMT shown in FIG. 2. Forthe purposes of reference, a narrow line cc is shown which indicates thecharacteristics of a general HEMT (hereinafter called “comparativeexample HEMT”) in which the lower electron supply layer 4 and upperelectron transport layer 5 are not disposed and the lower electrontransport layer 3 is in contact with the non-doped layer 6. In thisgeneral HEMT, a channel consisting of two-dimensional electron gas isgenerated at an interface between the lower electron transport layer 3and non-doped layer 6. A gate length was set to 0.8 μm and a unit gatewidth was set to 400 μm.

Consider now that the gate voltage Vg is changed gradually from a largenegative voltage close to 0. In the HEMT of the first embodiment, asindicated by the curve cp, as the gate voltage Vg exceeds about −2.25 V,the lower channel CH1 shown in FIG. 3 is generated and the drain currentId starts flowing. As the gate voltage Vg further increases, the draincurrent Id saturates once. In the range of the gate voltage Vg of about−1.6 V or higher, the upper channel CH0 is generated so that as the gatevoltage Vg increases, the drain current Id also increases. Although thegate voltage Vg is shown in the range of up to −1 V in FIG. 5, if thegate voltage Vg further increases, the drain current saturateseventually.

A slope of the graph in the range of the gate voltage Vg between −1.6 Vand −1 V is steeper than that in the range of the gate voltage Vg nothigher than −1.6 V. The reason, why a saturation current while only thelower channel CH1 is generated is smaller than that while also the upperchannel CH0 is generated, is that the two-dimensional electron gasdensity of the lower channel CH1 is sufficiently lower than that of theupper channel CH0.

In contrast, in the comparative example HEMT in which the lower channelCH1 is not generated, a drain current Id hardly flows until the gatevoltage Vg reaches about −1.6 V as indicated by the curve cc. In therange of the gate voltage Vg not lower than about −1.6 V, as the gatevoltage Vg increases, the drain current Id also increases, as in thecase of the HEMT of the first embodiment.

Therefore, in the HEMT of the first embodiment, the graph of the gatevoltage-drain current characteristics has a shape with an extendedgentle skirt.

A gate bias voltage Vgp is set so that a drain current la at no a.c.input voltage (idle current) is smaller than the saturation currentinduced by the lower channel CH1. When the amplitude of an input signalWpi is small, a drain current Id flows, substantially only through thelower channel CH1, and an output signal Wp0 is obtained.

In the comparative example HEMT, a gate bias voltage Vgc correspondingto the idle current la is higher than the gate bias voltage Vgp. When asignal Wci having the same amplitude as that of the input signal Wpi isinput, an output signal Wco is obtained. Since the slope of the curve ccnear at the gate bias voltage Vgc is steeper than that of the curve cpnear at the gate bias voltage Vgp, an amplitude of the output signal Wcois larger than that of the output signal Wpo, and the d.c. component ofthe drain current Id becomes large. Therefore, the d.c. component of theoutput power is large, and the efficiency is low.

In the HEMT of the first embodiment, since the amplitude of an outputsignal is small at a small input signal amplitude, it is possible tolower a gain and suppress an increase in the d.c. component of an outputpower.

As seen from FIG. 5, it is preferable to set the gate bias voltage insuch a manner that the HEMT applied to the peak amplifier operates inthe skirt region of the gate voltage-drain current characteristics whilean input signal amplitude is small. More specifically, it is preferableto set the gate bias voltage to such a value that the lower channel CH1of two-dimensional electron gas is generated in the lower electrontransport layer 3, but the upper channel CH0 is not generated in theupper electron transport layer 5.

It is preferable to broaden the skirt region of the gate voltage-draincurrent characteristics, in order to achieve a sufficient fall of thegain while an input signal is small. For example, it is preferable thata difference between a gate voltage at which the drain current is 5% ofthe saturation value and a gate voltage at which the drain current is 1%of the saturation value is at least 0.5 V.

FIG. 6A shows the relation between a gain and an input power of the HEMTof the first embodiment in respect of five values of idle current. Forthe purposes of comparison, FIG. 6B shows the relation between a gainand an input power of the comparative example HEMT in respect of eightvalues of idle current. The abscissa represents an input power in theunit of “dBm”, and the ordinate represents a gain in the unit of “dB”.In the first embodiment shown in FIG. 6A, the idle current was changedfrom 13 mA to 4.1 mA in five stages, and in the comparative exampleshown in FIG. 6B, the idle current was changed from 13 mA to 1.5 mA ineight stages.

In the HEMT of the first embodiment, it can be seen that as the idlecurrent is made small, the gain lowers considerably as the input powerlowers. This is because when the idle current is made small, the HEMToperates in the region where the slope of the gate voltage-drain currentcharacteristics cp shown in FIG. 5 is gentle. For example, when a gatebias voltage is set to obtain an idle current of 4.1 mA, the gainreaches maximum (about 24 dB) at an input power of about 10 dBm, and thegain declines to 9 dB at an input power of −10 dBm. A gain difference isabout 15 dB.

In contract, in the comparative example, even if the idle current ismade small, a large reduction in the gain does not appear because theslope of the gate voltage-drain current characteristics cc remainssteep. As the gate bias voltage is set to obtain an idle current of 1.5mA, a difference is at most 5 dB between a gain (about 19 dB) at aninput power of −10 dBm and the maximum gain (about 24 dB). Namely, inthe HEMT of the first embodiment, by properly setting the idle current,a difference can be made large between a gain at a small input power andthat at a large input power. For example, when the gate bias voltage isset to a voltage (in FIG. 5, Vg=−2.25 V) at which the drain currentstarts flowing, a difference between the maximum and minimum gains canbe set to at least 10 dB.

In the input/output characteristics of the Doherty amplifier shown inFIG. 9, the solid line ap indicates the input/output characteristics ofthe peak amplifier including the HEMT of the first embodiment, and thebroken line ap0 indicates the input/output characteristics of the peakamplifier including the comparative example HEMT. Particularly in thesmall input power region, an output power of the peak amplifierincluding the HEMT of the first embodiment is smaller than that of thepeak amplifier including the comparative example HEMT. This is because again at a small input power can be suppressed, as described withreference to FIG. 6A.

By using the HEMT of the first embodiment, an output of the peakamplifier at a small input power can be suppressed. Namely, an increasein the d.c. component of an output power can be suppressed. It istherefore possible to improve an efficiency of the Doherty amplifieritself.

If the amplifier is adopted at a base station, a distortion compensatingcircuit is generally combined with the amplifier to reduce leakage powerto adjacent channels. As the distortion compensating circuit, forexample, a digital pre-distortion (DPD) has been adopted, in whichdistortion is compensated by applying in advance a signal having inversecharacteristics of distortion to be generated. The carrier amplifierfrequently operates in the saturation region. Therefore, since a largepositive voltage is applied to the gate electrode, gate leak current islikely to increase. An increase in the gate leak current may causecollapse of distortion compensation. If an output power exceeds somelevel, distortion compensation is collapsed.

A Doherty amplifier using the conventional HEMT for each of the carrieramplifier and peak amplifier had an efficiency of 35% at a distortioncompensation collapsed point, whereas a Doherty amplifier using the HEMTof the first embodiment for the peak amplifier had an efficiency of 42%at a distortion compensation collapsed point. An efficiency of a Dohertyamplifier can thus be improved by using the HEMT of the first embodimentas the peak amplifier of the Doherty amplifier.

In the first embodiment described above, it is preferable to set anatomic ratio Al/(group III element) at the bottom of the lower electronsupply layer 4 to a range between 0.03 and 0.07. As the atomic ratioAl/(group III element) is made small, a density of two-dimensionalelectron gas in the lower channel CH1 becomes low, whereas as the atomicratio Al/(group III element) is made large, the density oftwo-dimensional electron gas becomes high. If the density oftwo-dimensional gas in the lower channel CH1 becomes too low, the lowerchannel CH1 is not generated substantially. As the two-dimensionalelectron gas density of the lower channel CH1 becomes high, thesaturation drain current induced by the lower channel CH1 shown in FIG.5 becomes large, and a flat region in the skirt region of the curve cpbecomes long. In this case, the efficiency lowers because a pinch-offcurrent is likely to flow in the high drain voltage region duringgate-off.

An atomic ratio Al/(group III element) at the upper surface of the lowerelectron supply layer 4 is preferable set to a range between 0 and 0.03.As the atomic ratio Al/(group III element) becomes large, latticemismatch becomes large at the interface between the upper electrontransport layer 5 and lower electron supply layer 4, and piezo chargesare accumulated so that a level at the lower end of the conduction bandof the energy band diagram is raised.

A concentration of n-type dopant of the lower electron supply layer 4 ispreferably set to a range between 1×10¹⁷ cm⁻³ and 5×10¹⁸ cm⁻³, and morepreferable to a range between 5×10¹⁷ cm⁻³ and 2×10¹⁸ cm⁻³. If aconcentration of n-type dopant is too low, an electron density lowers sothat sufficient electrons cannot be supplied to the lower channel CH1.Conversely, if the concentration of n-type dopant is made high, adensity of free electrons in the lower electron supply layer 4 becomeshigh. Free electrons in the lower electron supply layer 4 have amobility lower than that of electrons accumulated in the lower channelCH1, and negatively affect the operation of the HEMT. Further,electrical isolation between the source and drain electrodes becomesinsufficient.

A concentration of n-type dopant of the upper electron transport layer 5is preferably set to a range between 0 and 5×10¹⁷ cm⁻³, and morepreferably to a range between 0 and 1×10¹⁶ cm⁻³. If the concentration ofn-type dopant is high, a mobility of electrons accumulated in the upperchannel CH0 lowers.

A thickness of the lower electron supply layer 4 is preferably set to arange between 2 nm and 50 nm, and more preferably to a range between 5nm and 10 nm. A thickness of the upper electron supply layer 5 ispreferably set to a range between 5 nm and 100 nm, and more preferablyto a range between 10 nm and 50 nm. As the upper electron transportlayer 5 is thinned, a mobility of electrons accumulated in the upperchannel CH0 lowers. As the lower electron supply layer 4 is thickened,electrical isolation between the source and drain electrodes becomesinsufficient.

As a total thickness of the lower electron supply layer 4 and upperelectron transport layer 5 becomes thick, a distance between the lowerchannel CH1 and upper channel CH0 becomes long. As the distance becomeslong, a difference of gate-source capacitance becomes large between astate that only the lower channel CH1 is generated and a state that boththe lower and upper channels CH0 and CH1 are generated. As a changeamount of capacitance becomes large, there is a large difference ofphase characteristics between the carrier amplifier and peak amplifier.

In the first embodiment described above, although the lower electrontransport layer 3 is made of non-doped GaN, n-type dopant may be addedto a region of the lower electron transport layer 3 being in contactwith the lower electron supply layer 4. As n-type dopant is added, amobility of two-dimensional electron gas accumulated in the lowerchannel CH1 lowers. It is therefore possible to make gentler a slope ofthe skirt region of the gate voltage-drain current characteristics cpshown in FIG. 5.

The first embodiment adopts the configuration that the gain of the peakamplifier is suppressed at a small input power. As the input powerbecomes large, the HEMT of the carrier amplifier more frequentlyoperates in the saturation region, and gate leak current increases.Next, the second embodiment will be described which can suppress anincrease in the gate leak current of the HEMT of the carrier amplifier.

FIG. 7 is a cross sectional view of the HEMT according to the secondembodiment. Formed on a substrate 51 of SiC are an electron transportlayer 52 made of non-doped GaN, a non-doped layer 53 made of non-dopedAl_(0.25)Ga_(0.75)N and an electron supply layer 54 made of n-typeAl_(0.25)Ga_(0.75)N. A source electrode 57 and a drain electrode 58 aredisposed on the electron supply layer 54 at a distance from each other.

A protective layer 55 of n-type GaN covers the surface of the electronsupply layer 54 between the source electrode 57 and drain electrode 58.An insulating layer 56 of SiN is disposed on the protective layer 55. Agate electrode 59 is disposed in a partial surface area of theinsulating layer 56. The gate electrode 59 is disposed at a distancefrom both the source electrode 57 and drain electrode 58. A thickness ofthe insulating layer 56 is set to 20 nm. The HEMT of the secondembodiment has therefore not a Schottky gate structure but an insulatedgate structure.

FIG. 8 shows the relation between an output power of a Doherty amplifierand a leakage power to an adjacent channel. The abscissa represents anoutput power represented by a back-off amount from a saturation outputin the unit of “dB”, and the ordinate represents a leakage power to anadjacent channel in the unit of “dBc”. A solid line b1 in FIG. 8indicates the relation when the HEMT of the second embodiment is used inthe carrier amplifier, and a solid line b0 indicates the relation whenthe HEMT of the Schottky gate structure without the insulating film 56shown in FIG. 7 is used in the carrier amplifier.

When the HEMT of the Schottky gate structure is used, a leakage powerincreases abruptly at an output power of −8 dB. This means thatdistortion compensation is collapsed. When the HEMT of the secondembodiment having the insulated gate structure is used, distortioncompensation is not collapsed up to −6.2 dB. This is because an increasein forward gate leak current can be suppressed even while the carrieramplifier operates in the saturated region.

As described above, by using the HEMT of the insulated gate structure asthe carrier amplifier, it becomes possible to increase an output powerat the distortion compensation collapsed point and realize a highefficiency.

A gate length of the HEMT used for the carrier amplifier and peakamplifier is preferably set to a range between 0.3 μm and 0.7 μm, andmore preferably to a range between 0.5 μm and 0.6 μm. As the gate lengthis elongated, the gain of the Doherty amplifier lowers and distortioncharacteristics are deteriorated. If the gate length is shorter than 0.5μm, a breakdown voltage lowers to 200 V or lower. An efficiency lowersbecause of deterioration of pinch-off characteristics, and reliabilityof the device lowers.

A unit gate width is preferably set to a range between 200 μm and 350μm, and more preferably to a range between 250 μm and 300 μm. As theunit gate width is widened, the gain of the Doherty amplifier lowers,whereas as the unit gate width is narrowed, a maximum power to be outputlowers.

In the embodiments described above, although SiC is used as the materialof the substrate 1, substrates of other materials such as GaN, sapphireand Si may also be used. The upper electron supply layer 7 may be madeof AlGaInN instead of AlGaN. A threshold voltage of the HEMT can bechanged by controlling an atomic ratio In/(group III element) to adjusta band gap of the upper electron supply layer 4. Each of the electrontransport layer, electron supply layer and the like may be made of othercompound semiconductor material.

The present invention has been described in connection with thepreferred embodiments. The invention is not limited only to the aboveembodiments. It will be apparent to those skilled in the art that othervarious modifications, improvements, combinations, and the like can bemade.

1. A Doherty amplifier having a carrier amplifier and a peak amplifier,wherein the peak amplifier comprises a first field effect transistor andthe first field effect transistor comprises: a lower electron transportlayer made of compound semiconductor material; a lower electron supplylayer disposed over the lower electron transport layer and made ofcompound semiconductor material doped to n-type and having an electronaffinity smaller than an electron affinity of the lower electrontransport layer; an upper electron transport layer disposed over thelower electron supply layer and made of compound semiconductor materialhaving a doping concentration lower than a doping concentration of thelower electron supply layer or non-doped compound semiconductormaterial; an upper electron supply layer disposed over the upperelectron transport layer and made of n-type compound semiconductormaterial having an electron affinity smaller than an electron affinityof the upper electron transport layer; a source electrode and a drainelectrode disposed over the upper electron supply layer at a distancefrom each other and being in ohmic contact with the lower electrontransport layer and the upper electron transport layer; and a gateelectrode disposed over the upper electron supply layer between thesource electrode and the drain electrode.
 2. The Doherty amplifieraccording to claim 1, further comprises a bias circuit for applying ad.c. gate bias voltage to a gate electrode of the first field effecttransistor so as not to generate a channel at an interface between theupper electron transport layer and the upper electron supply layer, butto generate a channel at an interface between the lower electrontransport layer and the lower electron supply layer.
 3. The Dohertyamplifier according to claim 1, wherein the carrier amplifier includes asecond field effect transistor and the second field effect transistorcomprises: an electron transport layer made of compound semiconductormaterial; an electron supply layer disposed over the electron transportlayer and made of compound semiconductor material having an electronaffinity smaller than an electron affinity of the electron transportlayer; a source electrode and a drain electrode being in ohmic contactwith the electron transport layer; a gate electrode disposed over theelectron supply layer between the source electrode and the drainelectrode; and a gate insulating film made of insulating material anddisposed between the gate electrode and the electron supply layer.